| Product Form | Tensile (ksi) | .2% Yield (ksi) | Elongation % | Hardness (HRb) |
|---|---|---|---|---|
| Plate (.25”-1.75”) | 112 | 53 | 62 | 89 |
| Sheet (.038”-.15”) | 122 | 63 | 54 | 93 |
| Bar (.50”-5.50”) | 115 | 55 | 60 | 89 |
| Product Form | Tensile (ksi) | .2% Yield (ksi) | Elongation % |
|---|---|---|---|
| Bar | 110.0 | 52.6 | 62 |
| Plate | 107.4 | 50.3 | 67 |
| Sheet | 115.5 | 54.6 | 60 |
| Tube & Pipe | 105.4 | 45.4 | 70 |
| Product Form | Condition | Tensile (ksi) | .2% Yield (ksi) | Elongation (%) | Hardness (HRB) |
|---|---|---|---|---|---|
| Rod & Bar | Cold-Drawn | 80-100 | 25-50 | 35-55 | 65-85 |
| Rod & Bar | Hot-Finished | 80-100 | 30-50 | 35-55 | 65-85 |
| Tube & Pipe | Hot-Finished | 75-100 | 25-50 | 35*55 | - |
| Tube & Pipe | Cold-Drawn | 80-100 | 25-50 | 35-55 | 88 Max |
| Plate | Hot-Rolled | 80-105 | 30-50 | 35-55 | 65-85 |
| Sheet | Cold-Drawn | 80-100 | 30-45 | 35-55 | 88 Max |
| Temp° F | Tensile (psi) | .2% Yield (psi) | Elongation in 2 “ (%) |
|---|---|---|---|
| 70 | 144,000 | 84,000 | 44 |
| 400 | 134,000 | 66,000 | 45 |
| 600 | 132,000 | 63,000 | 42.5 |
| 800 | 131,500 | 61,000 | 45 |
| 1000 | 130,000 | 60,500 | 48 |
| 1200 | 119,000 | 60,000 | 34 |
| 1400 | 78,000 | 58,500 | 59 |
| 1600 | 40,000 | 39,000 | 117 |
| Product | Tensile (ksi) | .2% Yield (ksi) | Elongation (%) |
|---|---|---|---|
| Rod & Bar | 75-100 | 30-60 | 60-30 |
| Tensile (ksi) | .2% Yield (ksi) |
|---|---|
| 85 | 30-35 |
| Product Form | Condition | Tensile (ksi) | .2% Yield (ksi) | Elongation (%) | Hardness (HRB) |
|---|---|---|---|---|---|
| Rod & Bar | Annealed | 75-90 | 25-50 | 60-35 | 60-80 |
| Rod & Bar | Cold-Drawn Stress Relieved | 84-120 | 55-100 | 40-22 | 85-20 HRC |
| Plate | Annealed | 70-85 | 28-50 | 50-35 | 60-76 |
| Sheet | Annealed | 70-85 | 30-45 | 45-35 | 65-80 |
| Tube & Pipe Seamless | Annealed | 70-85 | 25-45 | 50-35 | 75 max * |
Product Form |
Condition |
Tensile (ksi) |
.2% Yield (ksi) |
Elongation % |
Hardness |
|---|---|---|---|---|---|
Rod & Bar |
Hot-Finished/Aged |
140-190 |
100-150 |
30-20 |
27-38 HRC |
Rod & Bar |
Hot Finished/Annealed |
90-110 |
40-60 |
45-25 |
75-90 HRB |
Rod & Bar |
Hot Finished/Annealed/Aged |
130-165 |
85-120 |
35-20 |
24-35 HRC |
Rod & Bar |
Cold-Drawn/Aged |
135-185 |
95-160 |
30-15 |
25-41 HRC |
Rod & Bar |
Cold-Drawn/Annealed/Aged |
130-190 |
85-120 |
30-20 |
24-35 HRC |
Plate |
Hot-Finished/Aged |
140-180 |
100-135 |
30-20 |
27-37 HRC |
Sheet |
Cold-Rolled/Annealed |
90-105 |
40-65 |
45-25 |
85 HRB Max |
| Material | Form and Condition | Tensile (ksi) | .2% Yield (ksi) | Elongation (%) | Hardness (HRB) |
|---|---|---|---|---|---|
| Rod & Bar | Hot Finished | 60-85 | 15-45 | 55-35 | 45-80 |
| Rod & Bar | Cold Drawn/Annealed or Hot-Finished/Annealed | 55-75 | 15-30 | 55-40 | 45-70 |
| Plate | Hot-Rolled/Annealed | 55-80 | 15-40 | 60-40 | 45-75 |
| Sheet | Annealed | 55-75 | 15-30 | 55-40 | 70 max |
| Tube & Pipe | Seamless Annealed | 55-75 | 12-30 | 60-40 | 70 max |
| Hardness, Knoop | 170 | 170 | |
| Hardness, Rockwell B | 80 | 80 | |
| Hardness, Vickers | 145 | 145 | |
| Tensile Strength, Ultimate | 344 MPa | 49900 psi | |
| Tensile Strength, Yield | 275 - 410 MPa | 39900 - 59500 psi | |
| Elongation at Break | 20 % | 20 % | |
| Reduction of Area | 35 % | 35 % | |
| Modulus of Elasticity | 105 GPa | 15200 ksi | In Tension |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poisson's Ratio | 0.37 | 0.37 | |
| Izod Impact | 114 - 171 J | 84.1 - 126 ft-lb | |
| Fatigue Strength | 300 MPa | 43500 psi | 1E+7 cycles, Unnotched |
| Fatigue Strength | 425 MPa | 61600 psi | 30,000 cycles, Unnotched |
| Fracture Toughness | 66 MPa-m½ | 60.1 ksi-in½ | K(Q); annealed |
| Shear Modulus | 45 GPa | 6530 ksi |
| Hardness, Brinell | 379 | 379 |
| Hardness, Knoop | 414 | 414 |
| Hardness, Rockwell C | 41 | 41 |
| Hardness, Vickers | 396 | 396 |
| Tensile Strength, Ultimate | 1170 MPa | 170000 psi |
| Tensile Strength, Yield | 1100 MPa | 160000 psi |
| Elongation at Break | 10 % | 10 % |
| Modulus of Elasticity | 114 GPa | 16500 ksi |
| Compressive Yield Strength | 1070 MPa | 155000 psi |
| Notched Tensile Strength | 1550 MPa | 225000 psi |
| Ultimate Bearing Strength | 2140 MPa | 310000 psi |
| Bearing Yield Strength | 1790 MPa | 260000 psi |
| Poisson's Ratio | 0.33 | 0.33 |
| Charpy Impact | 23 J | 17 ft-lb |
| Fatigue Strength | 160 MPa | 23200 psi |
| Fatigue Strength | 700 MPa | 102000 psi |
| Fracture Toughness | 43 MPa-m½ | 39.1 ksi-in½ |
| Shear Modulus | 44 GPa | 6380 ksi |
| Shear Strength | 760 MPa | 110000 psi |
| Hardness, Brinell | 200 | 200 |
| Hardness, Knoop | 222 | 222 |
| Hardness, Rockwell B | 75 | 75 |
| Hardness, Rockwell C | 11 | 11 |
| Hardness, Vickers | 209 | 209 |
| Tensile Strength, Ultimate | 344 MPa | 49900 psi |
| Tensile Strength, Yield | 275 - 410 MPa | 39900 - 59500 psi |
| Elongation at Break | 20 % | 20 % |
| Modulus of Elasticity | 105 GPa | 15200 ksi |
| Compressive Modulus | 110 GPa | 16000 ksi |
| Poisson's Ratio | 0.37 | 0.37 |
| Shear Modulus | 45 GPa | 6530 ksi |